High Chrome Alloy Casting Ball
|
|
|
C% |
Si % |
Mn % |
Cr% |
Mo % |
Cu % |
S% |
P% |
2.15~3.2 |
1.0max |
0.8~1.2 |
12~30 |
0.4~0.6 |
0.5max |
0.05max |
0.05max |
|
|
|
|
|
Through hardened, HRC 58~65 |
|
|
|
|
Low Chrome Alloy Casting Ball |
|
|
|
C% |
Si % |
Mn % |
Cr% |
Mo % |
Cu % |
S% |
P% |
2.15~3.2 |
1.0max |
0.8~1.2 |
1.2~2.0 |
0.4~0.6 |
0.5max |
0.05max |
0.05max |
|
|
|
|
|
Through hardened, HRC 60 Min |
|
|
|
|
Low Chrome Alloy Forging Ball |
|
|
|
C% |
Si % |
Mn % |
Cr% |
Mo % |
Cu % |
S% |
P% |
0.90~1.05 |
0.15~0.35 |
0.25~0.45 |
1.35~1.65 |
|
0.3max |
0.03max |
0.03max |
|
|
Hardness: |
through hardened, HRC 60 Min |
Grade: |
Milling Grade |
Size: |
20 mm~ 150 mm |
Application: |
Power plant, cement grinding, mining and chemical industries. |
|
|
|
|
|
|